Bulletproof Silicon Carbide Ceramics Armor For Ballistic Protection, Carborundum, Body Armor Plates, Vehicle Armor
Description:
Bulletproof Silicon Carbide Ceramics Armor utilizes the excellent physical properties of silicon carbide (SiC) ceramics to provide reliable ballistic protection for personnel, vehicles, and assets. Silicon carbide ceramics boast high hardness, high strength, low density, as well as good corrosion resistance and high-temperature performance, making them an ideal material for manufacturing bulletproof armor.
Feature:
1. High temperature tolerance,temperature up to 1600
2. Wear resistance
3. Corrosion resistance
4. High bending strength
5. high hardness
6.light weight
7.oxidation resistance
8.perfect efficiency of sealing
9.long time service life
10.Heat shock stability
11. Highly performance of mechanical strength
12.Cleaning or etching the hardest sub-surfaces
13.Used for grinding, lapping, and wire saw cutting as well as abrasive blasting
14.Self-lubrication
15.Lower thermal expansion coefficient
16. High thermal conductivity
17.All shape customized, can be square, hexagonal, cylindrical,or disc-like etc.
18. It is manufactured by pressureless sintering.or Reaction-Bonding
Applications:
Body Armor Plates
High-Tech Vehicle Armor Protection and Watercraft defence.
USA NIJ 0101.04 STANDARD:
| Class |
Test-bullet |
Bullet Weight
(g)
(gr.) |
Bullet Velocity
(m/s)
(ft/s) |
Distance
(m) |
Max. BFD
(mm) |
No. of Shots
per Panel |
No. of Test |
| I |
.22 Caliber LR
LRN |
2.6
40 |
329+-9
1080+-30 |
5 |
44 |
6 |
4 |
.380 ACP
FMJ RN |
6.2
95 |
322+-9
1055+-30 |
5 |
44 |
6 |
4 |
| II-A |
9mm
FMJ RN |
8.0
124 |
341+-9
1120+-30 |
5 |
44 |
6 |
4 |
.40S&W
FMJ RN |
11.7
180 |
322+-9
1055+-30 |
5 |
44 |
6 |
4 |
| II |
9mm
FMJ RN |
8.0
124 |
367+-9
1205+-30 |
5 |
44 |
6 |
4 |
.357 Mag
JSP |
10.2
158 |
436+-9
1430+-30 |
5 |
44 |
6 |
4 |
| III-A |
9mm
FMJ RN |
8.2
124 |
436+-9
1430+-30 |
5 |
44 |
6 |
4 |
.44 Mag
JHP |
15.6
240 |
436+-9
1430+-30 |
5 |
44 |
6 |
4 |
| III |
7.62mm Nato
FMJ |
9.6
148 |
847+-9
2780+-30 |
15 |
44 |
6 |
2 |
| IV |
.30 Calier
M2 AP |
10.8
166 |
878+-9
2880+-30 |
15 |
44 |
1 |
2 |
Technical data:
| Properties |
Units |
RSiC |
SiSiC |
SSiC |
| Bulk denstity SiC |
Vo1% |
≥99 |
≥85 |
≥99
|
| Bulk density |
g/cm3 |
2.60～2.72 |
3.01 |
3.10-3.15 |
| Apparent porosity |
% |
15 |
＜0.1 |
＜0.2 |
| Modulus of rupture at 20℃ |
Mpa |
80～90 |
250 |
400 |
| Modulus of rupture at 1200℃ |
Mpa |
90～100 |
280 |
650 |
| Modulus of elasticity at 20℃ |
Gpa |
- |
330 |
410 |
| Thermal Conductivity at 1200℃ |
w.m-1.k-1 |
35.0 |
45 |
55 |
| Thermal expansion at 1200℃ |
a×10-6/℃ |
4.60 |
4.5 |
4.0 |
| Thermal shock resistance at 1200℃ |
|
Very good |
Very good |
Very good |
| Max.working temperature |
℃ |
1650(oxid) |
1350 |
1600 |
Product Tags:
|
|